I am working with a product that has localized undercuts with a depth of 0.024" and currently a 45° release angle which is being stripped from the mold. Are there any processing suggestions to help with the ejection of this product? (i.e. mold temps, melt temps, cooling time, etc..)
Also would there be any suggested mold coatings that would reduce the required ejection forces with tritan TX2001?